Mount-Load Cell, JX-21JG389-M4-124-H21.3-AL, Aluminum machined parts for smart home manufacturing, smart catering equipment, kitchen equipment, ovens and freezers, surface treatment anodizing

6061 aluminum is a heat treatment that can be strengthened alloy, with good formability, weldability, and machinability while having medium strength, after annealing can still maintain good operability. 6061 aluminum's main alloying elements are magnesium and silicon, and the formation of the Mg2Si phase. If a certain amount of manganese and chromium, can neutralize the bad effects of iron; sometimes add a small amount of copper or zinc to improve the strength of the alloy, without making its corrosion resistance significantly reduced; conductive materials and a small amount of copper to offset the adverse effects of titanium and iron on the conductivity; zirconium or titanium can refine the grain and control recrystallization organization; in order to improve the machinability, can add lead and bismuth. In Mg2Si solid solution in aluminum, the alloy has an artificial age-hardening function.

Ultimate tensile strength of 6061: 205 Mpa

Yield strength under pressure: 55.2 Mpa

Coefficient of elasticity: 68.9 Gpa

Ultimate bending strength: 228 MPa

Bending yield strength: 103 MPa

F: Free processing state Applicable in the molding process, for the work hardening and heat treatment conditions special requirements of the product, the state of the product mechanical properties are not specified (uncommon)

O: annealed state Applicable to processed products with minimum strength obtained by complete annealing (occasionally occurs)

H: work-hardening state applicable to products that improve strength through work-hardening, the product can be processed after hardening (or not) to reduce the strength of additional heat treatment (generally non-heat treatment enhanced materials)

W: solid solution heat treatment state an unstable state, only applicable to the solution heat treatment, natural aging of the alloy at room temperature, the state code only indicates that the product is in the natural aging stage (not common)

T: Heat treatment state (different from F, O, H state) Applicable to heat treatment, after (or without) process hardening to achieve stability of the product. t code must be followed by one or more Arabic numerals (generally for heat-treatment reinforced materials) The state code behind our common non-heat treatment reinforced aluminum alloy is generally the letter H plus two digits. For example, 6061 T6.

High strength aluminum

6061T6 aluminum high strength, high hardness (up to HV90 degrees or more) good processing effect, good oxidation effect. No trachoma porosity, better flatness. Improve processing efficiency and reduce material cost. It will be the best choice for low-price and high-quality material. 6061-T6 series is an aluminum, magnesium, and silicon alloy, which is a heat treatment type corrosion-resistant alloy. Strength and corrosion resistance are very good, and uniformity is good.

1.6061 T6 high strength, high hardness (up to HV90 degrees or more), good processing effect, good oxidation effect. No trachoma, good flatness. Improve processing efficiency and reduce material cost. It will be the best choice for low-price and high-quality material. 6061-T6 series is an aluminum, magnesium, and silicon alloy, which is a heat treatment type corrosion-resistant alloy. The strength and corrosion resistance are very good, and the uniformity is good. 　The density of 6061 aluminum alloy is 0.0000028

2.6000 series aluminum alloy, whose main alloying elements are magnesium and silicon, has medium strength, good corrosion resistance, weldability, and good oxidation effect. It is widely used in various industrial structural parts that require certain strength (85-110 degrees) and high corrosion resistance, such as manufacturing trucks, tower buildings, ships, trams, railway vehicles, furniture and mechanical parts, precision machining, molds, etc.

Packing: Inner is Poly foam, out is carton. Then pallet. Carton size: 29*19*19.5CM and 23.5*17.5*8, CM and pallet size is: 215*100*90CM, or as your requirement.

Packing for CNC aluminum parts:

1. Usual packing: By pearl cotton/bubble bag/plastic wrap + carton box, 0.5-10kg/carton box.

2. Special packing(for large part/large quantity order): By pearl cotton/bubble bag/plastic wrap +carton box+wooden box.

3. As customers' requirement for CNC aluminum parts